P-Physical property
Granule Diameter:
15-53 um
Shape:
Sphere
Flow ability:
40 S (Hall current meter)
Apparent density:
4.3 g/cm3
Tap density:
8 g/cm3
Chemical composition
Fe:
Bal.
Co:
8.5～9.5 wt%
Ni:
17～19 wt%
Mo:
4.2～5.2 wt%
Mn:
≤0.1 wt%
Ti:
0.6～0.8 wt%
C:
AI:
S:
Cr:
Performance of molded parts
Density:
≥99.9%
Rm Tensile Strength:
About 1090 MPa (1930 MPa after heat treatment strengthening)
Yield Strength:
About 1000 MPa (1890 MPa after heat treatment strengthening)
Elongation:
About 4%
Elastic Modulus:
Approximately 160 GPa (180 GPa after heat treatment strengthening)
Hardness:
Approximately 35 HRC or 323 HB (After heat treatment, it can reach 55 HRC or 585 HB)